| Polyester Series (2): The general level - Injection Grade | |||||||||
| Applicable processing methods: injection grade | |||||||||
| Product Features: physical resistance, abrasion resistance, excellent shape, easy processing | |||||||||
| Applicable products: Sports round timber, decorative films, industrial round wood, shoes, electronic products, other | |||||||||
| Physical properties of species | Test methods | Unit | PU 75AIB | PU 80AI | PU 85AI | PU 90AI | PU 95AI | PU 98AI | PU 60DI |
| Proportion | ASTM D792 | kg/cm2 | 1.21±0.02 | 1.21±0.02 | 1.21±0.02 | 1.22±0.02 | 1.22±0.02 | 1.23±0.02 | 1.22±0.02 |
| Hardness | ASTM D2240 | Shore A Shore D | 80A±2 30D±2 | 82A±2 31D±2 | 86A±2 36D±2 | 90A±2 43D±2 | 94A±2 50D±2 | 97A±2 55D±2 | 97A±2 60D±2 |
| 100% Moduls | ASTM D412 | kg/cm2 | 40±10 | 55±15 | 70±15 | 80±15 | 110±15 | 150±15 | 170±15 |
| 300% Moduls | ASTM D412 | kg/cm2 | 80±10 | 100±10 | 110±10 | 120±10 | 200±15 | 260±15 | 280±15 |
| Tensile strength | ASTM D412 | kg/cm2 | 300±100 | 320±100 | 350±100 | 360±100 | 400±100 | 420±100 | 400±100 |
| Elongation | ASTM D412 | % | 700±100 | 680±100 | 600±100 | 550±100 | 550±100 | 500±100 | 400±100 |
| Tear strength | ASTM D624 | kg/cm2 | 70±15 | 85±15 | 90±15 | 110±15 | 120±15 | 150±15 | 160±15 |
| Abrasion resistance | DIN 53516 | mm3 | 120±15 | 120±15 | 130±15 | 130±15 | 110±15 | 100±15 | 100±15 |
| Compression ratio 70°Cx22hrs | ASTM D395 | % | |||||||
| properties | Transparent | Transparent | Transparent | Transparent | Transparent | Transparent | Transparent | ||
| Shrinkage | % | 2.2~2.8% | 1.5~2% | 1.5~2% | 1.5~2% | 1~1.5% | 1~1.5% | 1~1.5% | |
| Remarks | 1 The above data for reference only, the actual value due to detection test piece thickness varies slightly different specifications 2 recommended drying temperature: 90 ° C ~ 110 ° C room, drying time 3-4 hours 3 Packing 25KG / bag (can use color bag or empty bag to customer needs). | ||||||||
| Polyester Series (2): The general level - Injection Grade | |||||||||
| Applicable processing methods: injection grade | |||||||||
| Product Features: physical resistance, abrasion resistance, excellent shape, easy processing | |||||||||
| Applicable products: Sports round timber, decorative films, industrial round wood, shoes, electronic products, other | |||||||||
| Physical properties of species | Test methods | Unit | PU 64DI | PU 71DI | PU 71DID | ||||
| Proportion | ASTM D792 | kg/cm2 | 1.24±0.02 | 1.24±0.02 | 1.24±0.02 | ||||
| Hardness | ASTM D2240 | Shore A Shore D | 98A±2 64D±2 | 98A±2 70D±2 | 98A±2 72D±2 | ||||
| 100% Moduls | ASTM D412 | kg/cm2 | 220±15 | 270±15 | 2800±15 | ||||
| 300% Moduls | ASTM D412 | kg/cm2 | 320±15 | 320±15 | 330±15 | ||||
| Tensile strength | ASTM D412 | kg/cm2 | 400±100 | 400±100 | 420±100 | ||||
| Elongation | ASTM D412 | % | 430±100 | 450±100 | 450±100 | ||||
| Tear strength | ASTM D624 | kg/cm2 | 210±15 | 220±15 | 230±15 | ||||
| Abrasion resistance | DIN 53516 | mm3 | 100±15 | 100±15 | 100±15 | ||||
| Compression ratio 70°Cx22hrs | ASTM D395 | % | |||||||
| properties | 透明 | 透明 | 透明 | ||||||
| Shrinkage | % | 1~1.5% | 1~1.5% | 1~1.5% | |||||
| Remarks | 1 The above data for reference only, the actual value due to detection test piece thickness varies slightly different specifications 2 recommended drying temperature: 90 ° C ~ 110 ° C room, drying time 3-4 hours 3 Packing 25KG / bag (can use color bag or empty bag to customer needs). | ||||||||