Antistatic TPU:
Applicable processing methods: injection grade, extrusion grade
Product Features: physical resistance, excellent mobility, easy mold release, good processability
Applicable products: wire, straps, tubes, electronic parts, shoes, other
Physical
properties
of species

Test methods

Unit

PU
80ACM

PU
85ACM

PU
90ACM

PU
95ACM

PU
64ACM

PU
68ACM

　

Proportion

ASTM
D792

kg/cm2

1.21±0.02

1.21±0.02

1.21±0.02

1.21±0.02

1.22±0.02

1.22±0.02

　

Hardness

ASTM
D2240

Shore A
Shore D

83A±2
32D±2

87A±2
41D±2

90A±2
45D±2

95A±2
52D±2

98A±2
64D±2

99A±2
68D±2

　

100%
Moduls

ASTM
D412

kg/cm2

45±15

60±15

80±15

145±15

240±15

260±15

　

300%
Moduls

ASTM
D412

kg/cm2

100±15

130±15

160±15

230±15

330±15

340±15

　

Tensile
strength

ASTM
D412

kg/cm2

300±100

340±100

360±100

430±100

400±100

380±100

　

Elongation

ASTM
D412

%

400±100

420±100

470±100

500±100

400±100

430±100

　

Tear
strength

ASTM
D624

kg/cm2

85±15

90±15

120±15

140±15

200±15

230±15

　

Backwash
elasticity

DIN
53516

mm3

60±15　

60±15　

45±15　

45±15

40±15　

40±15

　

Static
coefficient

ASTM
D395

%

　

　

　

　

　

　

　

Resin
properties 

　

　

Transparent 

Transparent 

Transparent

Transparent 

Transparent 

透明

　

Shrinkage

　

%

1.5~2%

1.5~2%

1.5~2%

1.5~2%

1.5~2%

1~1.5%

　

Remarks

1 The above data for reference only, the actual value due to detection test piece

    thickness varies slightly different specifications
2 recommended drying temperature: 90 ° C ~ 110 ° C room, drying time 3-4 hours
3 Packing 25KG / bag (can use color bag or empty bag to customer needs).
4 antistatic antistatic masterbatch specifications available to do the adjustment.